不同抛光方法对牙科钴铬合金离子析出影响研究

童新文1，郑明1，程辉1，杨松1，许才明2   

  1. 作者单位：1.福建医科大学附属口腔医院修复科，口腔生物力学及美学研究中心，福州350002；2.福建出入境检验检疫局检验检疫技术中心，福州350001
  • 出版日期:2014-01-15 发布日期:2014-01-17
  • 通讯作者: 程辉
  • 基金资助:

    福建省卫生厅青年科研课题（2012-2-58）

Effect of different polishing methods on the ion release of Co-Cr dental alloy.

TONG Xin-wen*，ZHENG Ming，CHENG Hui，YANG Song，XU Cai-ming   

  1. *Department of Prosthodontics，Affiliated Stomatological Hospital，Fujian Medical University，Fuzhou 350002，China
  • Online:2014-01-15 Published:2014-01-17

PDF

摘要：

目的 比较不同抛光方法对钴铬合金离子析出的影响。方法 本研究于2013年3—8月在福建医科大学附属口腔医院进行。制作30个钴铬合金试样，随机分为5组，分别为砂纸抛光组、镜面抛光组、橡皮轮抛光组、电解抛光组和化学抛光组，每组6个试样。根据ISO 10271：2011标准采用浸泡实验检测试样Co、Cr离子的析出情况。检测腐蚀前的表面粗糙度和腐蚀前后表面形貌。结果 镜面抛光组Co、Cr析出量之和小于橡皮轮抛光组、电解抛光组和化学抛光组（P < 0.05）。化学抛光组表面粗糙度最大（P < 0.05）。化学抛光组Co、Cr析出量及其总和均大于砂纸抛光组、镜面抛光组、橡皮轮抛光组、电解抛光组（P < 0.05）。扫描电镜观察表明，砂纸抛光组、橡皮轮抛光组、化学抛光组表面有明显的腐蚀痕迹。结论 钴铬合金经镜面抛光可获得最好的表面形貌和抗腐蚀性能，化学抛光对钴铬合金表面形貌改善不大，其抗腐蚀性能最差。

关键词: 钴铬合金, 不同抛光方法, 表面粗糙度, 离子析出

Abstract:

Abstract：Objective To evaluate the effect of different polishing methods on ion element release of cobalt-chromium dental alloys. Methods Thirty cobalt-chromium dental alloys specimen were prepared and randomly divided into five groups，with six specimen in each group. The polishing methods were as follows：abrasive paper polishing，mirror polishing，rubber wheel polishing，electrolytic polishing and chemical polishing. An static immersion method was used in testing the ion release of Co，Cr of specimens. The surface roughness before immersion was tested and scanning electron microscope （SEM）was used to confirm the surface change of test specimens. Results Specimens polished by chemical got the roughest surface（P < 0.05）. The amount release of Co，Cr and the summation of five groups had significant difference（P < 0.05）. SEM results showed that the corrosive marks on the surface of specimens polished by abrasive paper，rubber wheel，electrolytic and chemical were very evident. There were not corrosive marks on the surface of mirror polishing group. Conclusion The mirror polishing may provide the smoothest surface and the best anti-corrosion performance for cobalt-chromium dental alloys，while chemical polishing does not make the surface of specimens smooth enough and then the specimens are more vulnerably corroded relatively.

Key words: Co-Cr dental alloy, different polishing methods, surface roughness, ion element release